Frequently Asked Questions About Hardfacing

All industries have parts and equipment that are exposed to some type of destructive wear.

For more Hard Surface Welding Wire Priceinformation, please contact us. We will provide professional answers.

Hardfacing is a cost-effective tool that will minimize wear and increase service life. At first glance, hardfacing can be confusing and troublesome. In reality, it isn't. Understanding some of the basics about hardfacing can go a long way toward instilling confidence in your hardfacing product selection.

Postle Industries, a manufacturer of hardfacing products, has found that the following 22 answers to frequently asked questions may help you select hardfacing products that are most appropriate for your application.

1. What is hardfacing?

Metal parts often fail their intended use not because they fracture, but because they wear by abrasion, impact, metal-to-metal contact or some other form of wear, which causes them to lose dimension and functionality. Hardfacing, also known as hard surfacing, is the application of a build-up or wear-resistant weld metal onto a part's surface by means of welding to extend the life of the part. The weld metal may be applied as a solid surface or in a pattern, such as a waffle pattern, herringbone or dot pattern, etc.

Hardfacing is becoming increasingly important for many industries to protect equipment that is exposed to wear and abrasion. Postle Industries produces products used in mining, dredging, recycling, farming, railroads, earthmoving and construction, cement, logging, power generation, oil and gas drilling, as well as steel making and forging. Extending the life of wear parts will save thousands of dollars and improve productivity. Hardfacing can be used to recondition parts that have already been exposed to wear and have lost their useful life, or used in the manufacture of new parts to improve their life before they are put into service.

There are three main types of hardfacing applications:

• Build-up or Rebuilding
• Hardfacing or Overlay
• A Combination of Build-up and Overlay

2. What base metals can be hardfaced?

Carbon and low-alloy steels with carbon contents of less than 1 percent can be hardfaced. Medium carbon and low-alloy steels are very common since they provide higher strength than mild steels and better abrasion resistance. High carbon alloys may require a special buffer layer.

The following base metals can be hardfaced:

• Stainless steels
• Manganese steels
• Carbon and alloy steels
• Cast irons
• Nickel-base alloys
• Copper-base alloys

Carbon and low-alloy steels are strongly magnetic and can easily be distinguished from austenitic manganese steel which is non-magnetic. There are many low-alloy and higher carbon steels that are used for manufacturing equipment and spare parts, especially equipment that requires higher strength and abrasion resistance. They are not easily differentiated but should be identified in order to determine proper preheat and post-heat temperature. As the alloy content increases, the need for preheat and post-heat becomes more critical.

For example, steel made from 4130 generally requires a preheat of 400ºF(200ºC). Steel used for rails is typically higher carbon and requires a minimum preheat of 600ºF to 700ºF (315ºC to 370ºC). Manganese steel does not require preheat. In fact, steps should be taken to keep the base metal heat below 500ºF (260ºC).

3. What are the most popular welding processes used to apply hardfacing?

In order of popularity, the following welding processes are used:

• Flux cored arc welding (FCAW) with open-arc or gas-shielded hardfacing wire
• Gas metal arc welding (GMAW) with gas-shielded wire
• Shielded metal arc welding (SMAW)
• Submerged arc welding (SAW)
• Gas tungsten arc welding (GTAW)
• Oxy-fuel welding (OFW) or oxyacetylene welding
• Plasma transferred arc welding, laser welding, thermal spray, and spray and fuse

There is a wide variety of equipment and power sources on the market. The current trend is toward the use of semi-automatic and automatic welding processes using FCAW and GMAW, which are about the same in terms of popularity. GMAW using either a solid wire or metal- cored welding wire must be used with a gas shield, whereas FCAW employs welding wires that are used open-arc or gasless, as well as with a gas shield. Shielded metal arc welding with flux- coated electrodes is still very popular, especially for field on-site hardfacing applications – equipment is inexpensive and portable. Factors to be considered when selecting a suitable welding process:

• Welding equipment availability, including size of power source Weld with stick electrode or semi-automatic wire
• Availability of hardfacing consumables Size of welding consumable
• Gas-shielded wire, open-arc wire, or submerged arc wire Operator skill available
• Welding location – indoors or outdoors
• Component size, shape and the area to be hardfaced Thickness of deposit
• Deposition rate
• Welding position – can the component be moved for welding in the flat position Machining requirements if any
• Desired finish (sub arc quality?)
• Component preparation for previously hardfaced parts
• Preheat and post welding treatments (temper/slow cool/air cool)

4. With so many welding processes available, which ones are the most economical?

Many factors affect the economics of hardfacing, but a major factor is the deposition rate. Table 1 shows the estimated deposition rate for each process.

5. Wear is such an all-encompassing term. Can it be broken down into more manageable categories?

Yes. Many different categories of wear exist— too many to cover in one article—but the most typical modes of wear are as follows (percentages are estimates of total wear):

• Abrasion—40 to 50 percent
• Impact—20 percent
• Metallic (metal to metal)—15 percent
• Heat—5 percent
• Corrosion—5 percent
• Other—5 percent

Tool Joint Hardfaced with Non-Cracking Duraband® NC

Most worn parts don't fail from a single mode of wear, such as impact, but from a combination of modes, such as abrasion and impact. For example, a mining bucket tooth usually is subjected to abrasion and impact, and depending on what type of material is mined (soft or hard rock), one mode may be more dominant than another. This will dictate the hardface welding product used.

Determining the wear mode or understanding the environment to which the part is exposed to is crucial to choosing which hardfacing alloy is best suited for the application. It can be challenging to select hardfacing products and may require trial and.

Most Common Types of Wear:

1. Abrasive Wear occurs when materials, such as grain, soil or sand, coal, or minerals slide across a metal surface. Abrasive Wear can be divided into gouging abrasion, high-stress grinding abrasion or low-stress scratching abrasion.
2. Impact Wear occurs when an object is struck by another object, such as a crusher part or a rail car wheel rolling over a manganese crossing, resulting in material flaking off or spalling.
3. Metal-to-Metal or Adhesive Wear – This occurs when two metallic surfaces slide against each other under pressure, creating a microwelding condition from frictional heat. Generally, found under non-lubricated or dry conditions

Grizzly Rotor and blades for Tire Shredding - hardfaced with Postle 2834 to prevent wear

6. Is there a convenient way to categorize the many hardfacing alloys that are available when determining which hardfacing alloy to use?

Yes. Iron-base alloys can be divided into four main categories:

• Martensitic – This includes all hardenable steels with Rockwell hardness from 20 to 65 HRC. Wire Products include Postalloy® 2892-MCG, 2898 -MCG, and Super Edge. Electrodes include Postalloy® 21 and 27. This group, similar to tool steel, hardens upon cooling. They are good for metal-to-metal and abrasive wear. They also can withstand a great deal of impact. The alloys below 45 HRC are generally used for build-up prior to hardfacing, or to restore dimension and the part must be machined after welding. Higher hardness martensitic alloys, above 50 HRC are used for abrasion resistance.
  
• Austenitic – Austenitic alloys include work-hardening manganese steels and stainless, such as Postalloy® 2850-FCO and Frogtuff-FCO wires or 205 and 207 Electrodes. This group is generally soft when welded and hardens only after the weld metal is worked under repeated impact.

  They have good impact properties and moderate abrasion resistance. Austenitic manganese steel is generally found around crushers, railroad track frogs and crossings, and shovel teeth. Stainless steels are good for corrosion resistance.

• Metal carbide and soft austenitic matrix – These alloys contain large amounts of metal carbides in softer matrix and are good for severe abrasion applications. The alloys that contain large amounts of chromium and carbon are known as the chromium carbide family and are closer to a cast iron or white iron. They sometimes contain additional amounts of niobium, vanadium and other elements. Their hardness's range from 40 HRC to 65 HRC. Alloys that contain large amounts of tungsten and carbon belong to the tungsten carbide family. Some contain small amounts of boron that form borides and are good for severe- abrasion applications. Products include Postalloy 2832-MCO, 2834-MCO, 2836-MCO wires and 214, 215HD or 218HD electrodes.
  
• Metal carbide in hard martensitic matrix – The martensitic matrix is essentially a tool steel with a hardness in the range of 45 HRC to 60 HRC. These alloys contain additions of niobium, vanadium, molybdenum or titanium. With proper procedures they can usually be applied without stress cracks. Products include Postalloy 2826NC-MCG and 2828NCTi-FCO.

7. Many hardfacing alloys crack. Is this normal?

It depends on the hardfacing alloy. Many chromium carbide alloys, such as Postalloy® 2834- MCO, check-crack when cooled to moderate temperatures; this is normal. Others, such as the austenitic and martensitic families, don't crack when applied with proper welding procedures.

8. What is check-cracking?

Check-cracking, or checking as it's sometimes called, occurs in the chromium carbide families and can be identified as cracks that are perpendicular to the bead length. They generally occur from 3/8” (8 mm) to 2”(50 mm) apart and are the result of high stresses induced by the contraction of weld metal as it cools.

The cracks propagate through the thickness of the weld bead and stop at the parent metal, as long as it's not brittle. In cases in which the parent metal is hard or brittle, you should select a buffer layer of a softer, tougher weld metal. The austenitic family is a good choice for a buffer deposit.

Stress Cracks in Chromium Carbide.

9. What is chromium carbide hardfacing?

Generally, these are iron-base alloys that contain high amounts of chromium (greater than 15 percent) and carbon (greater than 3 percent). These elements form hard carbides (chromium carbides) that resist abrasion. The deposits frequently check-crack about every 1⁄2-inch, which helps relieve stress from welding. Their low friction coefficient also makes them desirable in applications that require material with good slip.

Wire products include Postalloy 2820-MCO, 2832-MCO, and 2834-MCO. Electrodes include 214 and 215HD.

Generally speaking, the abrasion resistance increases as the amount of carbon and chromium increases, although carbon has the most influence. Hardness values range from 40 HRC to 65 HRC. They may also contain other elements that can form other carbides or borides that help increase wear resistance in high-temperature applications. These alloys are limited to two or three layers.

10. What are complex carbides?

Complex carbides generally are associated with the chromium carbide deposits that have additions of columbium (niobium), molybdenum, tungsten, or vanadium. The addition of these elements and carbon form their own carbides and/or combine with the present chromium carbides to increase the alloy's overall abrasion resistance. They can have all of these elements or just one or two. They are used for severe-abrasion or high-heat applications.

Products include Postalloy 2836-MCO or 218HD

11. What are carbides in martensite?

These are tool steel type alloys with numerous tightly packed carbides of titanium, niobium, vanadium or other elements. Carbides in martensite are an excellent choice for applications requiring crack-free deposits with good wear characteristics. Weld deposits generally exhibit the same wear resistant characteristics that are expected from chromium carbide hardfacing products. Since these alloys do not crack, they tend to be easier to apply in terms of reapplication.

Products include Postalloy 2826NC-MCG, Ultrashred 580, 2828-FCO

12. What is MIG Carbide?

This is also known as Tungsten Carbide Embedding. The tungsten carbide particles are fed from a hopper directly into the molten weld puddle of PS98. When the weld bead cools the resulting weld deposit contains large volumes of tungsten carbide particles embedded in a 55 to 60 HRC tool steel matrix. These extremely hard and wear-resistant particles protect bulldozer and grader blades, dragline and loader buckets, and many different types of hammers from premature wear in many challenging, highly abrasive applications.

13. What is meant by hardfacing pattern?

When working in rocky earth, ore or slag, the goal is to NOT trap the soil on the surface, but to protect the surface underneath from abrasion caused by the movement of the rocks over the surface. This can be done by applying a series of ridges or weld beads parallel to the flow of material, like rails. This will prevent the rocky soil from coming in contact with the surface.

When working in dirt or sand, apply hardface weld beads spaced from 1/4" (6.4 mm) to 1-1/2" (38 mm) apart and perpendicular or against the flow of an abrasive material. Forcing the material to compact between the weld beads works well for finely grained sands and soils.

Apply a dot pattern to areas that do not see heavy abrasion, but are subjected to wear, or when weld areas are hard to reach. A dot pattern is also used on thin base metals, when distortion and warpage may be an issue from overheating of the base metal.

When working in soil with some clay content, the goal is to use a hardfacing pattern that traps the soil on the surface, forming a layer of trapped soil that will protect the surface underneath. This is best done with a crosshatch or waffle pattern. This pattern also works well when there is a combination of fine and coarse soil.

14. Can hardness values be used to predict abrasion resistance?

No, this isn't a good idea. A martensitic alloy and a chromium carbide alloy can have the same hardness, let's say 58 HRC, and perform vastly different under the same abrasive conditions. A chromium carbide alloy will provide better abrasion resistance than a martensitic alloy. The metallurgical microstructure is a better measuring stick, but that isn't always available.

The only time hardness can be used to predict wear is when the alloys being evaluated are within the same family. For example, in the martensitic family, a 55 HRC alloy will have better abrasion resistance than a 35 HRC alloy. This may or may not be the case in either the austenitic or metal carbide families. Again, you have to consider the microstructure. You should consult with the manufacturer for recommendations.

15. If hardness is unreliable, then how is wear measured?

It depends on the type of wear involved, but in the case of abrasive wear—by far the most predominant wear mechanism—the ASTM Intl. G65 Dry Sand Rubber Wheel Test is used extensively. Essentially, this is a test in which the sample is weighed before and after the test, and the result is usually expressed in grams of weight loss or volume loss.

Are you interested in learning more about Sale Hardfacing Welding Wire? Contact us today to secure an expert consultation!

A sample is held against a spinning rubber wheel with a known force for a number of set number of revolutions. A specific type of sand, which is sized carefully, is trickled down between the sample and rubber wheel. This simulates pure abrasion, and the numbers are used as guidelines in material selection.

ASTM G65 Test Apparatus

16. What type of gas is used in GMAW hardfacing?

Low penetration and dilution are the major objectives in hardfacing, so pure argon and mixtures of argon with oxygen or carbon dioxide generally will produce the desired result. You also can use pure carbon dioxide, but you may get more spatter than you would with an argon mixture.

17. What is a ball, or globular, transfer, and why is it important?

Welding wires produce either a spray transfer or a globular (ball) transfer of molten metal across the welding arc. Spray transfer is a dispersion of fine molten metal drops and can be characterized as a smooth-sounding transfer. These wires are desirable in joining applications in which you require good penetration.

Ball transfer wires disperse larger molten metal drops, or balls. This type of transfer promotes low penetration and dilution, suitable for hardfacing. It has a noisier arc that produces an audible crackling sound and generally has a higher spatter level than spray transfer wires. Welding parameters such as electrical stick-out, gas (if any), amperage, and voltage can affect the size of the ball and its transfer. Gasless or open arc wires all have a globular or ball transfer.

18. Must parts be preheated before hardfacing?

Heat Affected Zone cracking is always a concern when welding low alloy and high carbon steels, and highly stressed parts or parts with complex shapes. As a general rule, all parts should be welded at least at room temperature. You should select higher preheat and interpass temperatures based on the base metal chemistry and hardfacing product you're using. High carbon steels will require preheating. For example, steel made from 4130 generally requires a preheat of 400°F(200°C). Steel for rails is typically high carbon and requires a minimum preheat of 600°F to 700°F (315°C to 370°C).

Manganese steel and some stainless steels require NO preheating, and welding temperatures should be kept as low as possible. In fact, steps should be taken to keep the manganese base metal below 500°F (260°C).

You should consult the manufacturer for the best combination to prevent cracking and spalling.

Preheating with Propane

19. When is a cobalt or nickel hardfacing alloy used?

Cobalt alloys contain many types of carbides and are good for severe abrasion at high temperatures. They also have good corrosion resistance for some applications. Deposit hardness ranges from 25 HRC to 55 HRC. Work-hardening alloys also are available.
Nickel-base alloys can contain chromium borides that resist abrasion. They can be good particularly in corrosive atmospheres and high temperatures when abrasion is a problem.

20. Why are some hardfacing products limited to two or three layers?

Chromium carbide, such as Postalloy 2834-MCO wire or complex carbides, such as 2836-MCO wire, are generally limited in the number of layers that can be applied. Electrodes include 214, 215HD or 218HD. The brittle nature of the metal carbides leads to check-cracking, and as multiple layers are applied, stress continues to build, concentrating at the root of the check cracks, until separation or spalling occurs between the parent metal or buffer and the hardfacing deposit.

Unless otherwise specified by the manufacturer, and with the correct procedures, martensitic hardfacing alloys, such as Postalloy 21 electrodes or 2898-FCO wire can be applied in multiple layers. Austenitic manganese hardfacing products, such as Postalloy 2850-FCO, can be applied in unlimited layers unless the manufacturer specifies otherwise.

Be sure to follow the manufactures recommendation pertaining to number of layers. If more layers are required a buffer or build-up alloy should be used.

21. What is meant by a build-up or buffer alloy?

These alloys are similar to the parent metal alloy in hardness and strength, with two main functions. Products that fit this category include Postalloy® 27 electrode and 2891-MCG- wires.

1. They are applied to severely worn parts to bring them back to dimension where machining must be used after welding. Hardness ranges from 30 HRC to 45 HRC.
2. They are applied as a buffer for subsequent layers of a more wear-resistant hardfacing deposit. If the hardfacing alloy produces check cracks, such as a chromium carbide alloy, then it's wise to use a tough manganese product as the buffer to blunt and stop the check cracks from penetrating into the base metal.

   A mild steel electrode, or wire such as 7018 or E70S6, should never be used for build-up or as a buffer layer. While mild steel welding products are great for joining and fabricating, they do not have the strength and hardness to support hardfacing. A soft mild steel buffer layer will collapse under the hardface layer, causing the hardface layer to spall off and fail.

22. Can cast iron be hardfaced?

Yes, but you consider preheat and interpass temperatures. Nickel and nickel-iron products usually are suitable for rebuilding cast iron. These products aren't affected by the carbon content of the parent metal and remain ductile. Multiple layers are possible. If further wear protection is required, metal carbide products can work well on top of the nickel or nickel-iron build-up.

These frequently asked questions only begin to address hardfacing. Hardfacing product manufacturers and specialists can contribute to a greater in-depth understanding of hardfacing and help assist you in product and process selection for your application.

Postalloy® is a registered trademark of Postle Industries, Inc.

At first glance, hardfacing can be confusing and troublesome; in reality, it isn't. Understanding some of the basics about hardfacing can go a long way toward instilling confidence in your hardfacing product selection.

The following 19 answers to frequently asked questions may help you select hardfacing products that are most appropriate for your application.

1. What is hardfacing?

Metal parts often fail their intended use not because they fracture, but because they wear, which causes them to lose dimension and functionality. Hardfacing, also known as hardsurfacing, is the application of buildup or wear-resistant weld metals to a part's surface by means of welding or joining.

2. What base metals can be hardfaced?

Carbon and low-alloy steels with carbon contents of less than 1 percent can be hardfaced. High-carbon alloys may require a special buffer layer.

The following base metals can be hardfaced:

• Stainless steels
• Manganese steels
• Cast irons and steels
• Nickel-base alloys
• Copper-base alloys

3. What is the most popular procedure used to apply hardfacing?

In order of popularity, the following procedures can be used:

• Flux cored arc welding (FCAW)
• Gas metal arc welding (GMAW)
• Shielded metal arc welding (SMAW)
• Submerged arc welding (SAW)
• Gas tungsten arc welding (GTAW)
• Oxyfuel welding (OFW) or oxyacetylene welding
• Plasma transferred arc welding, laser welding, thermal spray, and brazing

FCAW and GMAW may be interchangeable or the same in terms of popularity. However, the trend is toward use of semiautomatic and automatic welding procedures.

ProcedureDeposition Rate (lbs./hr.)FCAW8 to 25GMAW5 to 12SMAW3 to 5SAW8 to 25GTAW3 to 5OFW5 to 10

4. With so many welding processes available, which ones are the most economical?

Many factors affect the economics of hardfacing, but a major one is the deposition rate. Figure 1shows the estimated deposition rate for each process.

5. Wear is such an all-encompassing term. Can it be broken down into more manageable categories?

Yes. Many different categories of wear exist—too many to cover in one article—but the most typical modes of wear are as follows (percentages are estimates of total wear):

• Abrasion—40 percent
• Impact—25 percent
• Metallic (metal to metal)—10 percent
• Heat—5 percent
• Corrosion—5 percent
• Other—5 percent

Most worn parts don't fail from a single mode of wear, such as impact, but from a combination of modes, such as abrasion and impact. For example, a mining bucket tooth usually is subjected to abrasion and impact, and depending on what type of material is mined (soft or hard rock), one mode may be more dominant than another. This will dictate the welding product used.

Determining the wear mode can be challenging and may require trial and error when you select hardfacing products.

6. Is there a convenient way to categorize the many alloys when determining which hardfacing to use?

Yes. Iron-base alloys can be divided into three main categories:

• Martensitic. This includes all hardenable steels with Rockwell hardness from 20 to 65. This group, similar to tool steel, hardens upon cooling. They are good for metal-to-metal and abrasive wear. They also can withstand a great deal of impact.
• Austenitic. Austenitic alloys include work-hardening steels, such as manganese and stainless. This group generally is soft when it's welded and hardens only after the weld metal is worked. They have good impact properties and moderate abrasion resistance. The stainless steel family is good for corrosion resistance.
• Metal carbide. These alloys contain large amounts of metal carbides in a soft, tough matrix and are good for severe-abrasion applications. The alloys that contain large amounts of chromium and carbon are known as the chromium carbide family and are closer to a cast iron or white iron. Their hardnesses are from 40 HRC to 65 HRC. Alloys that contain large amounts of tungsten and carbon belong to the tungsten carbide family. Some contain small amounts of chromium and boron that form borides and are good for severe-abrasion applications.

7. Many hardfacing alloys crack. Is this normal?

It depends on the hardfacing alloy. Many chromium carbide alloys check-crack when cooled to moderate temperatures; this is normal. Others, such as the austenitic and martensitic families, don't crack when applied with proper welding procedures.

8. What is check-cracking?

Check-cracking, or checking as it's sometimes called, occurs in the metal carbide families and can be seen as cracks that are perpendicular to the bead length (see Figure 2). They generally occur from 3/8 to 2 inches apart and are the result of high stresses induced by the contraction of weld metal as it cools.

The cracks propagate through the thickness of the weld bead and stop at the parent metal, as long as it's not brittle. In cases in which the parent metal is hard or brittle, you should select a buffer layer of a softer, tougher weld metal. The austenitic family is a good choice for a buffer deposit.

9. What is chromium carbide hardfacing?

Generally, these are iron-base alloys that contain high amounts of chromium (greater than 18 percent) and carbon (greater than 3 percent). These elements form hard carbides (chromium carbides) that resist abrasion. The deposits frequently check-crack about every 1/2 in., which helps relieve stress from welding. Their low friction coefficient also makes them desirable in applications that require material with good slip.

Generally speaking, the abrasion resistance increases as the amount of carbon and chromium increases, although carbon has the most influence. Hardness values range from 40 HRC to 65 HRC. They also can contain other elements that can form other carbides or borides that help increase wear resistance in high-temperature applications. These alloys are limited to two or three layers.

10. What are complex carbides?

Complex carbides generally are associated with the chromium carbide deposits that have additions of columbium, molybdenum, tungsten, or vanadium. The addition of these elements and carbon form their own carbides and/or combine with the present chromium carbides to increase the alloy's overall abrasion resistance. They can have all of these elements or just one or two. They are used for severe-abrasion or high-heat applications.

11. Can hardness values be used to predict abrasion resistance?

No, this isn't a good idea. A martensitic alloy and a chromium carbide alloy can have the same hardness, let's say 58 HRC, and perform vastly different under the same abrasive conditions. The metallurgical microstructure is a better measuring stick, but that isn't always available.

The only time hardness can be used to predict wear is when the alloys being evaluated are within the same family. For example, in the martensitic family, a 55 HRC alloy will have better abrasion resistance than a 35 HRC alloy. This may or may not be the case in either the austenitic or metal carbide families. Again, you have to consider the microstructure. You should consult with the manufacturer for recommendations.

12. If hardness is unreliable, then how is wear measured?

It depends on the type of wear involved, but in the case of abrasive wear—by far the most predominant wear mechanism—the ASTM Intl. G65 Dry Sand Rubber Wheel Test is used extensively. This essentially is a test in which the sample is weighed before and after the test, and the result usually is expressed in grams of weight loss or volume loss.

A sample is held against a spinning rubber wheel with a known force for a number of revolutions. A specific type of sand, which is sized carefully, is trickled down between the sample and rubber wheel. This simulates pure abrasion, and the numbers are used as guidelines in material selection (seeFigure 3).

13. What type of gas is used in GMAW hardfacing?

Low penetration and dilution are the major objectives in hardfacing, so pure argon and mixtures of argon with oxygen or carbon dioxide generally will produce the desired result. You also can use pure carbon dioxide, but you'll get more spatter than you would with an argon mixture.

14. What is a ball, or globular, transfer, and why is it important?

Welding wires produce either a spray transfer or a globular (ball) transfer of molten metal across the welding arc. Spray transfer is a dispersion of fine molten metal drops and can be characterized as a smooth-sounding transfer. These wires are desirable in joining applications in which you require good penetration.

Ball transfer wires disperse larger molten metal drops, or balls. This type of transfer promotes low penetration and dilution, suitable for hardfacing. It has a noisier arc that produces an audible crackling sound and generally has a higher spatter level than spray transfer wires. Welding parameters such as electrical stickout, gas (if any), amperage, and voltage can affect the size of the ball and its transfer. Gasless, or open arc, wires all have a globular or ball transfer.

15. Must parts be preheated before hardfacing?

As a rule, you should bring all parts at least to room temperature. You can select higher preheat and interpass temperatures based on the base metal chemistry and hardfacing product you're using.

Manganese and some stainless steels and similar hardfacing products require no preheating, and welding temperatures should be kept as low as possible. Other steels usually require proper preheat and interpass temperatures. You should consult the manufacturer for the best combination to prevent cracking and spalling.

16. When is a cobalt or nickel hardfacing alloy used?

Cobalt alloys contain many types of carbides and are good for severe abrasion at high temperatures. They also have good corrosion resistance for some applications. Deposit hardness ranges from 25 HRC to 55 HRC. Work-hardening alloys also are available.
Nickel-base alloys can contain chromium borides that resist abrasion. They can be good particularly in corrosive atmospheres and high temperatures when abrasion is a problem.

17. Why are some hardfacing products limited to two or three layers?

Limited-layer products usually are in the metal carbide families, such as chromium carbide and tungsten carbide. You can apply martensitic and austenitic products in unlimited layers unless the manufacturer specifies otherwise.

The brittle nature of the metal carbides leads to check-cracking, and as multiple layers are applied, stress continues to build, concentrating at the root of the check cracks, until separation or spalling occurs between the parent metal or buffer and the hardfacing deposit.

18. What is meant by a buildup or buffer alloy?

These alloys often resemble the parent metal alloy and are applied to severely worn parts to bring them back to dimension or act as a buffer for subsequent layers of a more wear-resistant hardfacing deposit. If the hardfacing produces check cracks, then it's wise to use a tough manganese product as the buffer to blunt and stop the check cracks from penetrating into the base metal.

19. Can cast iron be hardfaced?

Yes, but you must take preheat and interpass temperatures into account. Nickel and nickel-iron products usually are suitable for rebuilding cast iron. These products aren't affected by the carbon content of the parent metal and remain ductile. Multiple layers are possible. If further wear protection is required, metal carbide products can work well on top of the nickel or nickel-iron buildup.

These frequently asked questions only begin to address hardfacing. Hardfacing product manufacturers and specialists can contribute to a greater in-depth understanding of hardfacing and help assist you in product and process selection for your application

Bob Miller is a materials and applications engineer at Postle Industries Inc., P.O. Box 42037, Cleveland, OH 44142, 216-265-9000, www.postle.com.